The Wedgwood scale (°W) is an obsolete temperature scale, which was used to measure temperatures above the boiling point of mercury of 356 °C (673 °F). The scale and associated measurement technique were proposed by the English potter Josiah Wedgwood in the 18th century. The measurement was based on the shrinking of clay when heated above red heat, and the shrinking was evaluated by comparing heated and unheated clay cylinders. The scale started at 1,077.5 °F (580.8 °C) being 0 °W and had 240 steps of 130 °F (54 °C). Both the origin and the step were later found inaccurate.
rdf:langString
ウェッジウッド温度（記号:°W）は、現在では用いられていない温度の単位である。水銀の沸点である356 ℃より高い温度を計測するために使われた。単位とそれを用いた計測の方法はイングランドの陶工であるジョサイア・ウェッジウッドによって、18世紀に開発された。この単位はより高温に加熱して焼結させたときの温度を基準にしている。この収縮については、加熱された粘土が入った円筒と、そうでない円筒を比較することで判断される。580.8 ℃は、ウェッジウッド温度では0 °Wとなり、72.2 ℃刻みに240個の目盛りが存在している。単位の起源並びにその目盛りは、後に両方とも不正確であったことが判明している。
rdf:langString
A Escala Wedgwood (°W) é uma obsoleta escala de temperatura inventada no século XVIII pelo ceramista britânico Josiah Wedgwood. Ela era usada para medir temperaturas acima do ponto de ebulição do mercúrio de 356 °C (673 °F). A medição era baseada no encolhimento da argila quando aquecida que ficava de coloração avermelhada, e o encolhimento foi avaliado comparando cilindros de argila aquecidos e não aquecidos. A escala começava em 1,077.5 °F (580.8 °C) sendo 0° Wedgwood e tinha 240 passos de 130 °F (54 °C). Tanto a origem e os passos foram encontrados mais tarde imprecisamente.
rdf:langString
Шкала́ Ве́джвуда (англ. Wedgwood scale, °W) — температурна шкала, що використовувалась для вимірювання температур вищих за точку кипіння ртуті — 356 °C (673 °F). Шкала і пов'язаний з нею метод вимірювання були запропоновані англійським художником-керамістом і дизайнером Джозайею Веджвудом у XVIII столітті. Вимірювання температури по шкалі Веджвуда ґрунтується на вимірюванні величини усадки глини при спіканні, шляхом порівняння довжини спечених і сирих глиняних циліндрів. Принцип вимірювання і числові характеристики шкали Веджвуда згодом були визнані неточними та вийшли з ужитку.
rdf:langString
Градус Уэджвуда — единица измерения температуры в температурной шкале, которая использовалась для измерения температуры выше точки кипения ртути — 356 °C (673 °F). Шкала и связанный метод измерения были предложены знаменитым английским художником-керамистом и дизайнером Джозайей Уэджвудом в XVIII веке. Измерение температуры по шкале Уэджвуда основано на измерении величины усадки глины при нагревании, путём сравнения длины нагретых и холодных глиняных цилиндров. Ноль по шкале Уэджвуда соответствует 580,8 °C (1077,5 °F), от него шкала была градуирована на 240 градусов до отметки 54 °C (130 °F). Принцип измерения и числовые характеристики шкалы Уэджвуда впоследствии были признаны неточными и вышли из употребления.
rdf:langString
rdf:langString
Wedgwood-Skala
rdf:langString
ウェッジウッド温度
rdf:langString
Escala Wedgwood
rdf:langString
Wedgwood scale
rdf:langString
Градус Уэджвуда
rdf:langString
Шкала Веджвуда
xsd:integer
30269981
xsd:integer
1112304723
rdf:langString
Die Wedgwood-Skala ist eine Temperaturskala für höhere Temperaturen, wie sie zum Beispiel bei der Porzellan- oder Metallherstellung auftreten. Sie ist nach dem britischen Unternehmer Josiah Wedgwood benannt, der sie 1782 vorschlug.
rdf:langString
The Wedgwood scale (°W) is an obsolete temperature scale, which was used to measure temperatures above the boiling point of mercury of 356 °C (673 °F). The scale and associated measurement technique were proposed by the English potter Josiah Wedgwood in the 18th century. The measurement was based on the shrinking of clay when heated above red heat, and the shrinking was evaluated by comparing heated and unheated clay cylinders. The scale started at 1,077.5 °F (580.8 °C) being 0 °W and had 240 steps of 130 °F (54 °C). Both the origin and the step were later found inaccurate.
rdf:langString
ウェッジウッド温度（記号:°W）は、現在では用いられていない温度の単位である。水銀の沸点である356 ℃より高い温度を計測するために使われた。単位とそれを用いた計測の方法はイングランドの陶工であるジョサイア・ウェッジウッドによって、18世紀に開発された。この単位はより高温に加熱して焼結させたときの温度を基準にしている。この収縮については、加熱された粘土が入った円筒と、そうでない円筒を比較することで判断される。580.8 ℃は、ウェッジウッド温度では0 °Wとなり、72.2 ℃刻みに240個の目盛りが存在している。単位の起源並びにその目盛りは、後に両方とも不正確であったことが判明している。
rdf:langString
A Escala Wedgwood (°W) é uma obsoleta escala de temperatura inventada no século XVIII pelo ceramista britânico Josiah Wedgwood. Ela era usada para medir temperaturas acima do ponto de ebulição do mercúrio de 356 °C (673 °F). A medição era baseada no encolhimento da argila quando aquecida que ficava de coloração avermelhada, e o encolhimento foi avaliado comparando cilindros de argila aquecidos e não aquecidos. A escala começava em 1,077.5 °F (580.8 °C) sendo 0° Wedgwood e tinha 240 passos de 130 °F (54 °C). Tanto a origem e os passos foram encontrados mais tarde imprecisamente.
rdf:langString
Шкала́ Ве́джвуда (англ. Wedgwood scale, °W) — температурна шкала, що використовувалась для вимірювання температур вищих за точку кипіння ртуті — 356 °C (673 °F). Шкала і пов'язаний з нею метод вимірювання були запропоновані англійським художником-керамістом і дизайнером Джозайею Веджвудом у XVIII столітті. Вимірювання температури по шкалі Веджвуда ґрунтується на вимірюванні величини усадки глини при спіканні, шляхом порівняння довжини спечених і сирих глиняних циліндрів. Принцип вимірювання і числові характеристики шкали Веджвуда згодом були визнані неточними та вийшли з ужитку.
rdf:langString
Градус Уэджвуда — единица измерения температуры в температурной шкале, которая использовалась для измерения температуры выше точки кипения ртути — 356 °C (673 °F). Шкала и связанный метод измерения были предложены знаменитым английским художником-керамистом и дизайнером Джозайей Уэджвудом в XVIII веке. Измерение температуры по шкале Уэджвуда основано на измерении величины усадки глины при нагревании, путём сравнения длины нагретых и холодных глиняных цилиндров. Ноль по шкале Уэджвуда соответствует 580,8 °C (1077,5 °F), от него шкала была градуирована на 240 градусов до отметки 54 °C (130 °F). Принцип измерения и числовые характеристики шкалы Уэджвуда впоследствии были признаны неточными и вышли из употребления.
xsd:nonNegativeInteger
5986